Title: Sintering  
Author: World Heritage Encyclopedia
Language: English
Subject: 3D printing, Frit, Sinter plant, Cemented carbide, Abnormal grain growth
Publisher: World Heritage Encyclopedia


Clinker nodules produced by sintering

Sintering is the process of compacting and forming a solid mass of material by heat[1] and/or pressure[2] without melting it to the point of liquefaction.

Sintering happens naturally in mineral deposits or as a manufacturing process used with metals, ceramics, plastics, and other materials. The atoms in the materials diffuse across the boundaries of the particles, fusing the particles together and creating one solid piece. Because the sintering temperature does not have to reach the melting point of the material, sintering is often chosen as the shaping process for materials with extremely high melting points such as tungsten and molybdenum. The study of sintering in metallurgy powder-related processes is known as powder metallurgy. An example of sintering can be observed when ice cubes in a glass of water adhere to each other, which is driven by the temperature difference between the water and the ice. Examples of pressure-driven sintering are the compacting of snowfall to a glacier, or the forming of a hard snowball by pressing loose snow together.

The word "sinter" comes from the Middle High German sinter, a cognate of English "cinder".

General sintering

Sintering is effective when the process reduces the porosity and enhances properties such as strength, electrical conductivity, translucency and thermal conductivity; yet, in other cases, it may be useful to increase its strength but keep its gas absorbency constant as in filters or catalysts. During the firing process, atomic diffusion drives powder surface elimination in different stages, starting from the formation of necks between powders to final elimination of small pores at the end of the process.

The driving force for densification is the change in free energy from the decrease in surface area and lowering of the surface free energy by the replacement of solid-vapor interfaces. It forms new but lower-energy solid-solid interfaces with a total decrease in free energy occurring on sintering 1-micrometre particles a 1 cal/g decrease. On a microscopic scale, material transfer is affected by the change in pressure and differences in free energy across the curved surface. If the size of the particle is small (and its curvature is high), these effects become very large in magnitude. The change in energy is much higher when the radius of curvature is less than a few micrometres, which is one of the main reasons why much ceramic technology is based on the use of fine-particle materials.[3]

For properties such as strength and conductivity, the bond area in relation to the particle size is the determining factor. The variables that can be controlled for any given material are the temperature and the initial grain size, because the vapor pressure depends upon temperature. Through time, the particle radius and the vapor pressure are proportional to (p0)2/3 and to (p0)1/3, respectively.[3]

The source of power for solid-state processes is the change in free or chemical potential energy between the neck and the surface of the particle. This energy creates a transfer of material through the fastest means possible; if transfer were to take place from the particle volume or the grain boundary between particles, then there would be particle reduction and pore destruction. The pore elimination occurs faster for a trial with many pores of uniform size and higher porosity where the boundary diffusion distance is smaller. For the latter portions of the process, boundary and lattice diffusion from the boundary become important.[3]

Control of temperature is very important to the sintering process, since grain-boundary diffusion and volume diffusion rely heavily upon temperature, the size and distribution of particles of the material, the materials composition, and often the sintering environment to be controlled.[3]

Ceramic sintering

Sintering is part of the firing process used in the manufacture of pottery and other ceramic objects. These objects are made from substances such as glass, alumina, zirconia, silica, magnesia, lime, beryllium oxide, and ferric oxide. Some ceramic raw materials have a lower affinity for water and a lower plasticity index than clay, requiring organic additives in the stages before sintering. The general procedure of creating ceramic objects via sintering of powders includes:

  • Mixing water, binder, deflocculant, and unfired ceramic powder to form a slurry;
  • Spray-drying the slurry;
  • Putting the spray dried powder into a mold and pressing it to form a green body (an unsintered ceramic item);
  • Heating the green body at low temperature to burn off the binder;
  • Sintering at a high temperature to fuse the ceramic particles together.

All the characteristic temperatures associated with phase transformation, glass transitions, and melting points, occurring during a sinterisation cycle of a particular ceramics formulation (i.e., tails and frits) can be easily obtained by observing the expansion-temperature curves during optical dilatometer thermal analysis. In fact, sinterisation is associated with a remarkable shrinkage of the material because glass phases flow once their transition temperature is reached, and start consolidating the powdery structure and considerably reducing the porosity of the material.

There are two types of sintering: with pressure (also known as hot pressing), and without pressure. Pressureless sintering is possible with graded metal-ceramic composites, with a nanoparticle sintering aid and bulk molding technology. A variant used for 3D shapes is called hot isostatic pressing.

To allow efficient stacking of product in the furnace during sintering and prevent parts sticking together, many manufacturers separate ware using ceramic powder separator sheets. These sheets are available in various materials such as alumina, zirconia and magnesia. They are additionally categorized by fine, medium and coarse particle sizes. By matching the material and particle size to the ware being sintered, surface damage and contamination can be reduced while maximizing furnace loading.

Sintering of metallic powders

Most, if not all, metals can be sintered. This applies especially to pure metals produced in vacuum which suffer no surface contamination. Sintering under atmospheric pressure requires the use of a protective gas, quite often endothermic gas.[4] Sintering, with subsequent reworking, can produce a great range of material properties. Changes in density, alloying, or heat treatments can alter the physical characteristics of various products. For instance, the Young's Modulus En of sintered iron powders remains insensitive to sintering time, alloying, or particle size in the original powder, but depends upon the density of the final product:

E_n/E = (D/d)^{3.4}

where D is the density, E is Young's modulus and d is the maximum density of iron.

Sintering is static when a metal powder under certain external conditions may exhibit coalescence, and yet reverts to its normal behavior when such conditions are removed. In most cases, the density of a collection of grains increases as material flows into voids, causing a decrease in overall volume. Mass movements that occur during sintering consist of the reduction of total porosity by repacking, followed by material transport due to evaporation and condensation from diffusion. In the final stages, metal atoms move along crystal boundaries to the walls of internal pores, redistributing mass from the internal bulk of the object and smoothing pore walls. Surface tension is the driving force for this movement.

A special form of sintering (which is still considered part of powder metallurgy) is liquid-state sintering in which at least one but not all elements are in a liquid state. Liquid-state sintering is required for making cemented carbide or tungsten carbide.

Sintered bronze in particular is frequently used as a material for bearings, since its porosity allows lubricants to flow through it or remain captured within it. Sintered copper may be used as a wicking structure in certain types of heat pipe construction, where the porosity allows a liquid agent to move through the porous material via capillary action. For materials that have high melting points such as molybdenum, tungsten, rhenium, tantalum, osmium and carbon, sintering is one of the few viable manufacturing processes. In these cases, very low porosity is desirable and can often be achieved.

Sintered metal powder is used to make frangible shotgun shells called breaching rounds, as used by military and SWAT teams to quickly force entry into a locked room. These shotgun shells are designed to destroy door deadbolts, locks and hinges without risking lives by ricocheting or by flying on at lethal speed through the door. They work by destroying the object they hit and then dispersing into a relatively harmless powder.

Sintered bronze and stainless steel are used as filter materials in applications requiring high temperature resistance while retaining the ability to regenerate the filter element. For example, sintered stainless steel elements are employed for filtering steam in food and pharmaceutical applications, and sintered bronze in aircraft hydraulic systems.

Sintering of powders containing precious metals such as silver and gold is used to make small jewelry items.


Particular advantages of the powder technology include:

  1. Very high levels of purity and uniformity in starting materials
  2. Preservation of purity, due to the simpler subsequent fabrication process (fewer steps) that it makes possible
  3. Stabilization of the details of repetitive operations, by control of grain size during the input stages
  4. Absence of binding contact between segregated powder particles – or "inclusions" (called stringering) – as often occurs in melting processes
  5. No deformation needed to produce directional elongation of grains
  6. Capability to produce materials of controlled, uniform porosity.
  7. Capability to produce nearly net-shaped objects.
  8. Capability to produce materials which cannot be produced by any other technology.
  9. Capability to fabricate high-strength material like turbine blades.
  10. After sintering the mechanical strength to handling becomes higher.

The literature contains many references on sintering dissimilar materials to produce solid/solid-phase compounds or solid/melt mixtures at the processing stage. Almost any substance can be obtained in powder form, through either chemical, mechanical or physical processes, so basically any material can be obtained through sintering. When pure elements are sintered, the leftover powder is still pure, so it can be recycled.


Particular disadvantages of the powder technology include:

  1. 100% sintered (iron ore) can not be charged in the blast furnace.
  2. By sintering one cannot create uniform sizes.

Plastics sintering

Plastic materials are formed by sintering for applications that require materials of specific porosity. Sintered plastic porous components are used in filtration and to control fluid and gas flows. Sintered plastics are used in applications requiring wicking properties, such as marking pen nibs. Sintered ultra high molecular weight polyethylene materials are used as ski and snowboard base materials. The porous texture allows wax to be retained within the structure of the base material, thus providing a more durable wax coating.

Liquid phase sintering

For materials which are difficult to sinter, a process called liquid phase sintering is commonly used. Materials for which liquid phase sintering is common are Si3N4, WC, SiC, and more. Liquid phase sintering is the process of adding an additive to the powder which will melt before the matrix phase. The process of liquid phase sintering has three stages:

  • Rearrangement – As the liquid melts capillary action will pull the liquid into pores and also cause grains to rearrange into a more favorable packing arrangement.
  • Solution-Precipitation – In areas where capillary pressures are high (particles are close together) atoms will preferentially go into solution and then precipitate in areas of lower chemical potential where particles are not close or in contact. This is called "contact flattening". This densifies the system in a way similar to grain boundary diffusion in solid state sintering. Ostwald ripening will also occur where smaller particles will go into solution preferentially and precipitate on larger particles leading to densification.
  • Final Densification – densification of solid skeletal network, liquid movement from efficiently packed regions into pores.

For liquid phase sintering to be practical the major phase should be at least slightly soluble in the liquid phase and the additive should melt before any major sintering of the solid particulate network occurs, otherwise rearrangement of grains will not occur. Liquid phase sintering was successfully applied to improve grain growth of thin semiconductor layers from nanoparticle precursor films.[5]

Electric current assisted sintering

These techniques employ electric currents to drive or enhance sintering.[6] English engineer A. G. Bloxam registered in 1906 the first patent on sintering powders using direct current in vacuum. The primary purpose of his inventions was the industrial scale production of filaments for incandescent lamps by compacting tungsten or molybdenum particles. The applied current was particularly effective in reducing surface oxides that increased the emissivity of the filaments.[7]

In 1913, Weintraub and Rush patented a modified sintering method which combined electric current with pressure. The benefits of this method were proved for the sintering of refractory metals as well as conductive carbide or nitride powders. The starting boroncarbon or silicon–carbon powders were placed in an electrically insulating tube and compressed by two rods which also served as electrodes for the current. The estimated sintering temperature was 2000 °C.[7]

In the United States, sintering was first patented by Duval d’Adrian in 1922. His three-step process aimed at producing heat-resistant blocks from such oxide materials as zirconia, thoria or tantalia. The steps were: (i) molding the powder; (ii) annealing it at about 2500 °C to make it conducting; (iii) applying current-pressure sintering as in the method by Weintraub and Rush.[7]

Sintering that uses an arc produced via a capacitance discharge to eliminate oxides before direct current heating, was patented by G. F. Taylor in 1932. This originated sintering methods employing pulsed or alternating current, eventually superimposed to a direct current. Those techniques have been developed over many decades and summarized in more than 640 patents.[7]

Of these technologies the most well known is resistance sintering (also called Electro Sinter Forging is the latest advancement in this field.

Spark plasma sintering

In spark plasma sintering (SPS), external pressure and an electric field are applied simultaneously to enhance the densification of the metallic/ceramic powder compacts. This densification uses lower temperatures and shorter amount of time than typical sintering.[8] For a number of years, it was speculated that the existence of sparks or plasma between particles could aid sintering; however, Hulbert and coworkers systematically proved that the electric parameters used during spark plasma sintering make it (highly) unlikely.[9] In light of this, the name "spark plasma sintering" has been rendered obsolete. Terms such as "Field Assisted Sintering Technique" (FAST), "Electric Field Assisted Sintering" (EFAS), and Direct Current Sintering (DCS) have been implemented by the sintering community.[10] Using a DC pulse as the electric current, spark plasma, spark impact pressure, joule heating, and an electrical field diffusion effect would be created.[11]

Electro Sinter Forging

Capacitor discharge sintering. Is is under use for the production of diamond metal matrix composites and under evaluation for the production of hard metals,[12] nitinol [13] and other metals and intermetallics. It is characterized by a very low sintering time allowing machines to sinter at the same speed as a compaction press.

Pressureless sintering

Pressureless sintering is the sintering of a powder compact (sometimes at very high temperatures, depending on the powder) without applied pressure. This avoids density variations in the final component, which occurs with more traditional hot pressing methods.

The powder compact (if a ceramic) can be created by slip casting into a plaster mould, then the final green compact can be machined if necessary to final shape before being heated to sinter.

Densification, vitrification and grain growth

Sintering in practice is the control of both densification and grain growth. Densification is the act of reducing porosity in a sample thereby making it more dense. Grain growth is the process of grain boundary motion and Ostwald ripening to increase the average grain size. Many properties (mechanical strength, electrical breakdown strength, etc.) benefit from both a high relative density and a small grain size. Therefore, being able to control these properties during processing is of high technical importance. Since densification of powders requires high temperatures, grain growth naturally occurs during sintering. Reduction of this process is key for many engineering ceramics.

For densification to occur at a quick pace it is essential to have (1) an amount of liquid phase that is large in size, (2) a near complete solubility of the solid in the liquid, and (3) wetting of the solid by the liquid. The power behind the densification is derived from the capillary pressure of the liquid phase located between the fine solid particles. When the liquid phase wets the solid particles, each space between the particles becomes a capillary in which a substantial capillary pressure is developed. For submicrometre particle sizes, capillaries with diameters in the range of 0.1 to 1 micrometres develop pressures in the range of 175 pounds per square inch (1,210 kPa) to 1,750 pounds per square inch (12,100 kPa) for silicate liquids and in the range of 975 pounds per square inch (6,720 kPa) to 9,750 pounds per square inch (67,200 kPa) for a metal such as liquid cobalt.[3]

Densification requires constant capillary pressure where just solution-precipitation material transfer would not produce densification. For further densification, additional particle movement while the particle undergoes grain-growth and grain-shape changes occurs. Shrinkage would result when the liquid slips between particles and increase pressure at points of contact causing the material to move away from the contact areas forcing particle centers to draw near each other.[3]

The sintering of liquid-phase materials involves a fine-grained solid phase to create the needed capillary pressures proportional to its diameter and the liquid concentration must also create the required capillary pressure within range, else the process ceases. The vitrification rate is dependent upon the pore size, the viscosity and amount of liquid phase present leading to the viscosity of the overall composition, and the surface tension. Temperature dependence for densification controls the process because at higher temperatures viscosity decreases and increases liquid content. Therefore, when changes to the composition and processing are made, it will affect the vitrification process.[3]

Sintering mechanisms

Sintering occurs by diffusion of atoms through the microstructure. This diffusion is caused by a gradient of chemical potential – atoms move from an area of higher chemical potential to an area of lower chemical potential. The different paths the atoms take to get from one spot to another are the sintering mechanisms. The six common mechanisms are:

  • Surface diffusion – Diffusion of atoms along the surface of a particle
  • Vapor transport – Evaporation of atoms which condense on a different surface
  • Lattice diffusion from surface – atoms from surface diffuse through lattice
  • Lattice diffusion from grain boundary – atom from grain boundary diffuses through lattice
  • Grain boundary diffusion – atoms diffuse along grain boundary
  • Plastic deformation – dislocation motion causes flow of matter

Also one must distinguish between densifying and non-densifying mechanisms. 1–3 above are non-densifying – they take atoms from the surface and rearrange them onto another surface or part of the same surface. These mechanisms simply rearrange matter inside of porosity and do not cause pores to shrink. Mechanisms 4–6 are densifying mechanisms – atoms are moved from the bulk to the surface of pores thereby eliminating porosity and increasing the density of the sample.

Grain growth

A grain boundary(GB) is the transition area or interface between adjacent crystallites (or grains) of the same chemical and lattice composition, not to be confused with a phase boundary. The adjacent grains do not have the same orientation of the lattice thus giving the atoms in GB shifted positions relative to the lattice in the crystals. Due to the shifted positioning of the atoms in the GB they have a higher energy state when compared with the atoms in the crystal lattice of the grains. It is this imperfection that makes it possible to selectively etch the GBs when one wants the microstructure visible.[14] Striving to minimize its energy leads to the coarsening of the microstructure to reach a metastable state within the specimen. This involves minimizing its GB area and changing its topological structure to minimize its energy. This grain growth can either be normal or abnormal, a normal grain growth is characterized by the uniform growth and size of all the grains in the specimen. Abnormal grain growth is when a few grains grow much larger than the remaining majority.[15]

Grain boundary energy/tension

The atoms in the GB are normally in a higher energy state than their equivalent in the bulk material. This is due to their more stretched bonds, which gives rise to a GB tension \sigma_{GB}. This extra energy that the atoms possess is called the grain boundary energy, \gamma_{GB}. The grain will want to minimize this extra energy thus striving to make the grain boundary area smaller and this change requires energy.[15]

“Or, in other words, a force has to be applied, in the plane of the grain boundary and acting along a line in the grain-boundary area, in order to extend the grain-boundary area in the direction of the force. The force per unit length, i.e. tension/stress, along the line mentioned is σGB. On the basis of this reasoning it would follow:

\sigma_{GB} dA \text{ (work done)} = \gamma_{GB} dA \text{ (energy change)}\,\!

with dA as the increase of grain-boundary area per unit length along the line in the grain-boundary area considered.”[15] [pg 478]

The GB tension can also be thought of as the attractive forces between the atoms at the surface and the tension between these atoms is due to the fact that there is a larger interatomic distance between them at the surface compared to the bulk (i.e. surface tension). When the surface area becomes bigger the bonds stretch more and the GB tension increases. To counteract this increase in tension there must be a transport of atoms to the surface keeping the GB tension constant. This diffusion of atoms accounts for the constant surface tension in liquids. Then the argument,

\sigma_{GB} dA \text{ (work done)} = \gamma_{GB} dA \text{ (energy change)}\,\!

holds true. For solids, on the other hand, diffusion of atoms to the surface might not be sufficient and the surface tension can vary with an increase in surface area.[16] For a solid, one can derive an expression for the change in Gibbs free energy, dG, upon the change of GB area, dA. dG is given by

\sigma_{GB} dA \text{ (work done)} = dG \text{ (energy change)} = \gamma_{GB} dA + A d\gamma_{GB}\,\!

which gives

\sigma_{GB} = \gamma_{GB} + \frac{Ad\gamma_{GB}}{dA}\,\!

\sigma_{GB} is normally expressed in units of \frac{N}{m} while \gamma_{GB} is normally expressed in units of \frac{J}{m^2} (J = Nm) since they are different physical properties.[15]

Mechanical equilibrium

In a two-dimensional isotropic material the grain boundary tension would be the same for the grains. This would give angle of 120° at GB junction where three grains meet. This would give the structure a hexagonal pattern which is the metastable state (or mechanical equilibrium) of the 2D specimen. A consequence of this is that to keep trying to be as close to the equilibrium as possible. Grains with fewer sides than six will bend the GB to try keep the 120° angle between each other. This results in a curved boundary with its curvature towards itself. A grain with six sides will, as mentioned, have straight boundaries while a grain with more than six sides will have curved boundaries with its curvature away from itself. A grain with six boundaries (i.e. hexagonal structure) are in a metastable state (i.e. local equilibrium) within the 2D structure.[15] In three dimensions structural details are similar but much more complex and the metastable structure for a grain is a non-regular 14-sided polyhedra with doubly curved faces. In practice all arrays of grains are always unstable and thus always grows until its prevented by a counterforce.[17]

Grains strive to minimize their energy, and a curved boundary has a higher energy than a straight boundary. This means that the grain boundary will migrate towards the curvature. The consequence of this is that grains with less than 6 sides will decrease in size while grains with more than 6 sides will increase in size.[18]

Grain growth occurs due to motion of atoms across a grain boundary. Convex surfaces have a higher chemical potential than concave surfaces therefore grain boundaries will move toward their center of curvature. As smaller particles tend to have a higher radius of curvature and this results in smaller grains losing atoms to larger grains and shrinking. This is a process called Ostwald ripening. Large grains grow at the expense of small grains. Grain growth in a simple model is found to follow:

G^m= G_0^m+Kt

Here G is final average grain size, G0 is the initial average grain size, t is time, m is a factor between 2 and 4, and K is a factor given by:

K= K_0 e^{\frac{-Q}{RT}}

Here Q is the molar activation energy, R is the ideal gas constant, T is absolute temperature, and K0 is a material dependent factor.

Reducing grain growth

Solute ions

If a dopant is added to the material (example: Nd in BaTiO3) the impurity will tend to stick to the grain boundaries. As the grain boundary tries to move (as atoms jump from the convex to concave surface) the change in concentration of the dopant at the grain boundary will impose a drag on the boundary. The original concentration of solute around the grain boundary will be asymmetrical in most cases. As the grain boundary tries to move the concentration on the side opposite of motion will have a higher concentration and therefore have a higher chemical potential. This increased chemical potential will act as a backforce to the original chemical potential gradient that is the reason for grain boundary movement. This decrease in net chemical potential will decrease the grain boundary velocity and therefore grain growth.

Fine second phase particles

If particles of a second phase which are insoluble in the matrix phase are added to the powder in the form of a much finer powder than this will decrease grain boundary movement. When the grain boundary tries to move past the inclusion diffusion of atoms from one grain to the other will be hindered by the insoluble particle. Since it is beneficial for particles to reside in the grain boundaries and they exert a force in opposite direction compared to the grain boundary migration. This effect is called the Zener effect after the man who estimated this drag force to

F = \pi r \lambda \sin (2\theta)\,\!

where r is the radius of the particle and λ the interfacial energy of the boundary if there are N particles per unit volume their volume fraction f is

f = \frac{4}{3} \pi r^3 N\,\!

assuming they are randomly distributed. A boundary of unit area will intersect all particles within a volume of 2r which is 2Nr particles. So the number of particles n intersecting a unit area of grain boundary is:

n = \frac{3f}{2 \pi r^2}\,\!

Now assuming that the grains only grow due to the influence of curvature, the driving force of growth is \frac{2 \lambda}{R} where (for homogeneous grain structure) R approximates to the mean diameter of the grains. With this the critical diameter that has to be reached before the grains ceases to grow:

n F_{max} = \frac{2 \lambda}{D_{crit}}\,\!

This can be reduced to D_{crit} = \frac{4r}{3f} \,\! so the critical diameter of the grains is dependent of the size and volume fraction of the particles at the grain boundaries.[19]

It has also been shown that small bubbles or cavities can act as inclusion

More complicated interactions which slow grain boundary motion include interactions of the surface energies of the two grains and the inclusion and are discussed in detail by C.S. Smith.[20]

Natural sintering in geology

Petrifying spring in Réotier near Mont-Dauphin, France

In geology a natural sintering occurs when a mineral spring brings about a deposition of chemical sediment or crust, for example as of porous silica.[21]

A sinter is a mineral deposit that presents a porous or vesicular texture; its structure shows small cavities. These may be siliceous deposits or calcareous deposits.[22]

Siliceous sinter is a deposit of opaline or amorphous silica which appears as incrustations near hot springs and geysers. It sometimes forms conical mounds, called geyser cones, but can also form as a terrace. The main agents responsible for the deposition of siliceous sinter are algae and other vegetation in the water. Altering of wall rocks can also form sinters near fumaroles and in the deeper channels of hot springs. Examples of siliceous sinter are geyserite and fiorite. They can be found in many places, including Iceland, New Zealand, and Yellowstone National Park and Steamboat Springs in the USA.

Calcareous sinter is also called tufa, calcareous tufa, or calc-tufa. It is a deposit of calcium carbonate, as with travertine. Called petrifying springs, they are quite common in limestone districts. Their calcareous waters deposit a sintery incrustation on surrounding objects. The precipitation is assisted with mosses and other vegetable structures, thus leaving cavities in the calcareous sinter after they have decayed.[22]

Petrifying spring at Pamukkale, Turkey:

See also


  1. ^ "Sinter, v." Oxford English Dictionary Second Edition on CD-ROM (v. 4.0) © Oxford University Press 2009
  2. ^ The Free Dictionary"Sinter" accessed May 1, 2014
  3. ^ a b c d e f g
  4. ^
  5. ^
  6. ^
  7. ^ a b c d
  8. ^
  9. ^ Hulbert, D. M. et al. The Absence of Plasma in‘ Spark Plasma Sintering’. Journal of Applied Physics 104, 3305 (2008).
  10. ^ Anselmi-Tamburini, U. et al. in Sintering: Nanodensification and Field Assisted Processes (Castro, R. & van Benthem, K.) (Springer Verlag, 2012).
  11. ^
  12. ^ A.Fais Discharge sintering of hard metal cutting tools. International Powder Metallurgy Congress and Exhibition, Euro PM 2013 (
  13. ^ C.Balagna et al Electro-sinter-forged Ni–Ti alloy. Intermetallics 68, pp.31-41 (2016) (
  14. ^
  15. ^ a b c d e
  16. ^
  17. ^
  18. ^
  19. ^
  20. ^
  21. ^ Sinter in
  22. ^ a b sinter in Encyclopedia Britanica.

Further reading

External links

  • Particle-Particle-Sintering – a 3D lattice kinetic Monte Carlo simulation
  • Sphere-Plate-Sintering – a 3D lattice kinetic Monte Carlo simulation
This article was sourced from Creative Commons Attribution-ShareAlike License; additional terms may apply. World Heritage Encyclopedia content is assembled from numerous content providers, Open Access Publishing, and in compliance with The Fair Access to Science and Technology Research Act (FASTR), Wikimedia Foundation, Inc., Public Library of Science, The Encyclopedia of Life, Open Book Publishers (OBP), PubMed, U.S. National Library of Medicine, National Center for Biotechnology Information, U.S. National Library of Medicine, National Institutes of Health (NIH), U.S. Department of Health & Human Services, and, which sources content from all federal, state, local, tribal, and territorial government publication portals (.gov, .mil, .edu). Funding for and content contributors is made possible from the U.S. Congress, E-Government Act of 2002.
Crowd sourced content that is contributed to World Heritage Encyclopedia is peer reviewed and edited by our editorial staff to ensure quality scholarly research articles.
By using this site, you agree to the Terms of Use and Privacy Policy. World Heritage Encyclopedia™ is a registered trademark of the World Public Library Association, a non-profit organization.

Copyright © World Library Foundation. All rights reserved. eBooks from World Library are sponsored by the World Library Foundation,
a 501c(4) Member's Support Non-Profit Organization, and is NOT affiliated with any governmental agency or department.